Investigation of the influence of boundary conditions and degradation factor of the surface layer on the GTE structural elements stress-strain state https://doi.org/10.33108/visnyk_tntu2017.04.097
Article Sidebar
Main Article Content
Abstract
The influence of the boundary conditions of the nonstationary thermal cyclic loading and degradation of the material surface layers on the stress-strain state of the material of the wedge-shaped specimens, which model the gas-turbine engine blade edge, is shown using the methods of physical and mathematical
modeling with the presence of crack-type defects. The necessity of the investigation of structural changes and properties of the material, thermal and thermal-deformed state of the material is demonstrated to determine the possibilities of safe extension of the given lifetime of the equipment and assurance of efficiency as well as reliability of energy systems.
Article Details
Issue
Section
This work is licensed under a Creative Commons Attribution 4.0 International License.
References
1. Tret'yachenko G.N., Kravchuk L.V., Kuriat R.I., et al., Thermal Fatigue of Materials under Conditions of Inhomogeneous Thermal Stressed State, Naukova Dumka, Kiev, 1985, 278 p. [in Russian].
2. Getsov L.B., Materials and Strength of the Components of Gas Turbines, Nedra, Moscow, 591 p. [in Russian].
3. Bensch M., Sato A., Warnken N., Affeldt E., Reed R.C., Glatzel U. Modelling of High Temperature Oxidation of Alumina-Forming Single-Cristal Nickel-Base Superalloys, Acta Materialia, Vol. 60, Is. 15, 2012, pp. 5468 – 5480.
4. Sato А., Chiu Y.-L., Reed R.C. Oxidation of nickel-based single-crystal superalloys for industrial gas turbine applications, Acta Materialia, Vol. 59, 2011, pp. 225 – 240.
5. Buiskikh K.P., Kiselevskaya S.G., Kravchuk L.V., Zadvornyi E.A., Feofentov N.N. Kinetics and Mechanisms of Degradation of the Surface Layers of Gas-Turbine Engine Structural Components Under Cyclic Thermal Loading During Initiation and Propagation of Thermal Fatigue Crack, Strength of Materials, Vol. 48, Is. 6, 2016, pp. 64 – 72.
6. DSTU 2367-94. Unified System of Protection against Corrosion and Aging. Refractory Metals, Alloys, and Coatings. A Method for Testing for High-Temperature Corrosion and Thermal Fatigue in a Flow of the Combustion Products of Fuel [in Ukrainе], Kiev, Valid since February 25, 1994.
7. Kravchuk L.V., Kuriat R.I., Buiskikh K.P., Zadvornyi E.A., Kiselevskaya S.G. Study of Damage Kinetics of Heat-Resistant Alloys Subjected to Thermocyclic Loading in a Gas Flow, Strength of Materials, Vol. 382 (38), Is. 4, 2006, pp. 386 – 391.
8. Kravchuk L.V., Kuriat R.I., Buiskikh K.P., Kiselevskaya S.G. Surface Layers' Degradation of Heat-Resistant Alloys and Thermal Fatigue Damageability of Gas Turbine Engine Structural Components, Strength of Materials, Vol. 395 (40), Is. 5, 2008, pp. 552 – 559.